Marín, J.C.; Barroso, A.; París, F.; Cañas, J. - In: Energy 33 (2008) 7, pp. 1068-1083
The inspection of damages detected in some blades of 300kW wind turbines revealed that the nature of these damages was probably due to a fatigue mechanism. The causes that had originated the failure (superficial cracks, geometric concentrator, abrupt change of thickness) have been studied,...