DENDRITIC GROWTH OF THE BINARY SUCCINONITRILE-CAMPHOR SYSTEM
Succinonitrile (SCN)–2 wt% Camphor (CAMP) alloy was unidirectionally solidified with a constant temperature gradient (G = 3.01 K/mm) at different growth rates (V = 6.5–113 μm/s) and with a constant growth rate (V = 6.5 μm/s) at different temperature gradients (G = 1.93 - 3.01 K/mm). Microstructural parameters (primary dendrite arm spacings, λ1, secondary dendrite arm spacings, λ2, dendrite tip radius, R, and mushy zone depth, d) were measured as a function of growth rate and temperature gradient. The experimental results have been compared with theoretical models and previous experimental works. The stability constant (σ) for this alloy system was calculated and compared with similar experimental results.
Year of publication: |
2007
|
---|---|
Authors: | ÇADIRLI, E. ; KAYA, H. |
Published in: |
Surface Review and Letters (SRL). - World Scientific Publishing Co. Pte. Ltd., ISSN 1793-6667. - Vol. 14.2007, 06, p. 1169-1179
|
Publisher: |
World Scientific Publishing Co. Pte. Ltd. |
Subject: | Dendrites | directional solidification | organic compounds |
Saved in:
Online Resource
Saved in favorites
Similar items by subject
-
ÇADIRLI, E., (2009)
-
ŞAHIN, M., (2010)
-
An analysis of heating fuel market behavior, 1989--1990
(2008)
- More ...
Similar items by person
-
ÇADIRLI, E., (2009)
-
ŞAHIN, M., (2010)
- More ...