Enhanced thermal conductivity and thermal performance of form-stable composite phase change materials by using [beta]-Aluminum nitride
[beta]-Aluminum nitride powder is a promising additive due to its great conductivity value, which can enhance the thermal conductivity of organic phase change materials. In this paper, a high conductivity form-stable phase change material was prepared by blending polyethylene glycol, silica gel, and [beta]-Aluminum nitride powder. The conductivity value of the composite PCMs was determined using the Hotdisk thermal analyzer, which is based on the transient plane source technique. Experiment of heat storage and release performance was carried out to investigate heat efficiencies of TES system. The results showed that thermal conductivity of composite PCMs increased with an increase in [beta]-Aluminum nitride content, but the value of latent heat decreased correspondingly. There was no change on the melting temperature while different ratios of composites. The value of thermal conductivity changed from 0.3847Â WÂ m-1Â K-1 to 0.7661Â WÂ m-1Â K-1 with the increase of mass ratio of [beta]-Aluminum nitride from 5% to 30%. The heat storage and release rate of the composite PCMs was higher than that of pure polyethylene glycol.
Year of publication: |
2009
|
---|---|
Authors: | Wang, Weilong ; Yang, Xiaoxi ; Fang, Yutang ; Ding, Jing ; Yan, Jinyue |
Published in: |
Applied Energy. - Elsevier, ISSN 0306-2619. - Vol. 86.2009, 7-8, p. 1196-1200
|
Publisher: |
Elsevier |
Keywords: | Polyethylene glycol Silica gel [beta]-Aluminum nitride Thermal conductivity |
Saved in:
Online Resource
Saved in favorites
Similar items by person
-
Wang, Weilong, (2009)
-
Wang, Weilong, (2009)
-
Wang, Weilong, (2014)
- More ...