Synthesis of Mesoporous Tio2-Al2o3 Composites Supported Niw Hydrotreating Catalysts and Their Superior Catalytic Performance for Heavy Oil Hydrodenitrogenation
Mesoporous TiO2-Al2O3 composites with different Ti/Al molar ratios were successfully synthesized via pre-hydrolysis co-precipitation method and the corresponding NiW supported hydrotreating (HDT) catalysts were prepared via incipient wetness co-impregnation method. The effects of Ti modification on the physicochemical properties of the prepared supports and catalysts were determined by the characterization techniques such as XRD, ICP-OES, N2 physical adsorption-desorption, FTIR, NH3-TPD, H2-TPR, HRTEM and XPS. Finally, quinoline, indole and coker gas oil (CGO) were used respectively as probes to investigate the Ti modification on the hydrodenitrogenation (HDN) performances of the corresponding catalysts. The results show that the TiO2-Al2O3 samples synthesized by the pre-hydrolysis co-precipitation method achieved the level of molecular composition, and the crystalline structures, pore properties and acidity properties of the TiO2-Al2O3 supports varied with the Ti/Al molar ratios; Ti modification can modulate the interaction between the active metals and the supports (MSI), and the incorporation of TiO2 can also promote the formation of more so-called “type II” NiWS active phases and enhance the sulfidation degrees of active metals; furthermore, the existence of Ti3+ species acted as an electron donor weakened the bond energy between the active metals and sulfur atoms and further promoted the formation of more CUS. The catalytic assessment results show that the HDN activities of the catalysts were effectively improved after Ti modification and the improvement was largely due to the promotion of the cleavage of the C(sp3)-N bond of basic nitrides and the C(sp2)-N bond of non-basic nitrides. Superior catalytic performance was observed over the NiW/TA1 catalyst due to its suitable pore properties, moderate MSI, large number of CUS, moderate stacking and high active metal sulfidation degree of the active phase
Year of publication: |
[2022]
|
---|---|
Authors: | Huang, Wenbin ; zhou, yasong ; Wei, Qiang ; Liu, Xiaodong ; Zhang, Pengfei ; Xu, Zhusong ; Yu, Zhiqing ; Wang, Xiaohan ; Liu, Haoran ; Dai, Xiaojun ; Yang, Han |
Publisher: |
[S.l.] : SSRN |
Saved in:
freely available
Saved in favorites
Similar items by person
-
Xiao, Zhihua, (2022)
-
4 Volatility-Managed Portfolio Strategies
Liu, Haoran, (2020)
-
Chuang, O-Chia, (2023)
- More ...